ER310           符合：YB/T5092 H12Cr26Ni21Si

不銹鋼焊絲                           相當：AWS A5.9 ER310

        ISO 14343-A-G 25 20

                                     In accordance with：YB/T5092 H12Cr26Ni21Si

Be equivalent to：AWS A5.9 ER310

ISO 14343-A-G 25 20

說明：焊絲主要成分是25Cr-20Ni，是不銹鋼MIG、TIG焊接材料，可全位置焊接。耐高溫性能穩定，可達1200℃。焊接作業性極佳—送絲順暢、電弧穩定、成形美觀、飛濺極少；熔敷金屬的機械性能穩定。

用途：常用于耐高溫產品如高溫爐、煤炭焦化設備等，也可應用于復合層堆焊和異種鋼的焊接。

Instructions：The ER310 welding stick consists mainly of 25Cr-20Ni. It belongs to stainless steel MIG and TIG welding material and can be used to all-position welding. It has stable performance to resist high temperature up to 1200℃. It performs well while welding, with smooth wire feed, stable voltaic arc, beautiful formation and little splatter. The deposited metal has steady mechanical property.

Use：It’s usually used to weld heat resistance products, such as high temperature furnace and coal coke equipment. It can also be used to weld composite layer and dissimilar steel.

 

焊絲化學成分（%）

 

參考電流（DC+）

焊絲直徑（mm）	Φ0.8	Φ1.0	Φ1.2	Φ1.6	Φ2.0	Φ2.5	Φ3.2
焊接電流（A）	70～150	100～200	140～220	50～100	100～200	200～300	300～400

注意事項：

1.      保護氣體：注意保護氣體的純度，混合氣配比推薦Ar+1～3%O2。TIG采用純Ar。

2.      氣體流量：20～25L/min。

3.      干伸長度：15～25mm。

4.      將焊接部位的銹層、濕氣、油污、灰塵等確實除凈。

5.      室外焊接時，當風速大于1.5m/s應采取適當的防風措施，以防發生氣孔。

6.      以上建議僅供參考，在具體操作中以現場情況為準。必要時先進行工藝評定再確定焊接方案。