黑龍江L302斯米克Ag25Cu40銀焊條經銷商L302 Wire & rod 絲 745-775 Ag25 Cu40 Zn Rem. Brazing of copper, copper alloys, steel and stainless steel etc. 釬焊銅及銅合金、鋼及不銹鋼等

Category 類 別	Trade- Mark 牌 號	Equivalent to China Standard 相當國標	Characteristics & application 特性和用途	Equivalent to AWS 相當AWS
Hard-surfacing 硬 面 堆 焊	D 667	EDZCr-B-15	HRc≥48. Resistance to wear, gas corrosion and oxidation. Hardfacing of blast furnace hopper and cracker part. HRc≥48，耐磨、耐氣蝕、抗氧化。堆焊高爐料鐘、破碎機件
	D 802	EDCoCr-A-03	HRc38-47. Resistance to heat, wear and corrosion. Hardfacing of high temperature part such as the edge of thermo-cutter. HRc38-47，耐熱、耐蝕、耐磨。堆焊高溫工件如熱剪切刀刃	ECoCr-A
	D 812	EDCoCr-B-03	HRc45-50. Resistance to heat, wear and corrosion. Hardfacing of high temperature part such as internal-combustion engine valve. HRc45-50，耐熱、耐蝕、耐磨。堆焊高溫工件如內燃機閥	ECoCr-B
	D 822		HRc≥53. Resistance to Wear and heat, bad shock resistance. Hardfacing of rotating blade wheel of boiler. HRc≥53，耐熱、耐磨，但抗沖擊性差。堆焊鍋爐旋轉葉輪
	D 832	EDCoCr-C-03	HRc≥50. Wear and heat resistance. Hardfacing of high temperature part such as hot-rolling guided way. HRc≥50，耐熱、耐磨。堆焊高溫工件如熱軋導軌	ECoCr-C
	D 842	EDCoCr-D-03	HRc28-38. Corrosion and thermo-fatigue resistance, work harding. Hardfacing of hot forging die. HRc28-38，耐蝕、抗熱疲勞，具有加工硬化性。堆焊熱鍛模
Cast iron 鑄 鐵	Z 308	EZNi	Pure nickel, excellent general properties. Used to weld thin cast iron part and repair welding machined surface, such as guided way of machine tool. 純鎳，綜合性能好。鑄鐵薄件及加工面補焊用，如機床導衛	ENi-Cl
	Z 408	EZNiFe	Iron nickel, high strength and excellent ductility. Repair welding of important gray cast iron and nodular cast iron, such as cylinder cap. 鎳鐵，強度高、塑性好。重要灰鑄鐵及球鐵焊補用，如汽缸蓋	ENiFe-Cl
	Z 508	EZNiCu-1	Copper nickel, good machinability and bad crack resistance. Repair welding of sand hole and gray cast iron machined surface subject to no load. 鎳銅，易加工，但抗裂性較差。不受力的灰鑄鐵加工面及砂眼補焊	ENiCu-B
Copper alloys 銅 合 金	Cu 107	ECu	Red copper, atmosphere and sea water corrosion and excellent electric conductivity. Welding of red copper such as electrical copper row. 紫銅，耐大氣，海水腐蝕，導電性好。紫銅焊接用，如導電銅排	ECu
	Cu 207	ECuSi	Silicon bronze, corrosion resistance and high strength. Welding of copper, silicon bronze and brass. 硅青銅，耐蝕、強度高。銅、硅青銅及黃銅焊接用	ECuSi
	Cu 227	ECuSnB	Tin phosphor bronze, corrosion resistance and high strength. Welding of copper, silicon bronze and brass. 錫磷青銅，耐蝕、強度高。銅、硅青銅及黃銅焊接用	ECuSn-C
	Cu 237	ECuAl	Aluminum bronze, wear and corrosion and high strength. Welding or surfacing of copper alloys. 鋁青銅，耐磨、耐蝕，強度高。銅合金焊接或堆焊用	ECuAl-A2
Aluminum alloys 鋁 合 金	Al 109	TAl	Pure aluminum, excellent corrosion resistance and middle strength. Welding of pure aluminum. 純鋁，耐蝕性好，但強度不高，純鋁焊接用	E1100
	Al 209	TAlSi	Silicon aluminum, good crack resistance and wide range of usage. Welding of aluminum alloys other than aluminum magnesium alloys. 鋁硅，抗裂性好，通用性大。鋁合金焊接用，不宜焊接鋁鎂合金	E4043
	Al 309	TAMn	Manganese aluminum, corrosion resistance and high strength. Welding of aluminum alloys. 鋁錳，強度高，耐蝕。鋁合金焊接用	E3003
Nickel alloys 鎳合金	Ni 102	ENi-1	Pure nickel. Welding and surfacing of nickel and nickel to steel. 純鎳，用于鎳、鎳與鋼的焊接與堆焊	ENi-1
	Ni 207	ENiCu-7	Copper nickel. Welding and surfacing of copper nickel and copper nickel to steel. 鎳銅，用于鎳銅、鎳銅與鋼的焊接與堆焊	ENiCu-7

Category 類 別	Trade mark 牌 號	Chemical composition 主要成份(%)	Characteristics & application 特性和用途	Equivalent to AWS 相當AWS
Hardfacing 硬 面 堆 焊	S 101	C3 Cr28 Ni4 Si3.5 Fe Rem.	HRc48-54. Resistance to wear, gas corrosion and oxidation. Hardfacing of bucket tooth and case pump. HRc48-54，耐磨、耐氣蝕、抗氧化。堆焊鏟斗齒，泵套
	S 111	C1 Cr29 W5 Co Rem.	HRc38-47. Resistance to wear and corrosion at high-temperature. Hardfacing of high temperature and pressure valve. HRc38-47，高溫下耐磨、耐蝕。堆焊高溫高壓閥門	ECoCr-A
	S 112	C1.5 Cr29 W8 Co Rem.	HRc45-50. Resistance to wear and corrosion at high-temperature. Hardfacing of valve and hot-rolling pass. HRc45-50，高溫下耐磨、耐蝕。堆焊閥門，熱軋孔型	ECoCr-B
	S 113	C2.5 Cr30 W17 Co Rem.	HRc≥55. Wear and heat resistance at high temperature, bad shock resistance. Hardfacing of screw charging carriage. HRc≥55，高溫下耐磨、耐熱，但抗沖擊性差。堆焊螺旋送料機用
	S 114	C2.5 Cr30 W12 Co Rem.	HRc≥53. Wear and heat resistance at high temperature, bad shock resistance. Hardfacing of three-cone bit. HRc≥53，高溫下耐磨、耐熱，但抗沖擊較差。堆焊牙輪鉆頭	ECoCr-C
Copper alloys   銅 　 合 　 金	S 201	Sn1 Si0.3Mn0.3 Cu Rem.	Good mechanical properties and crack resistance. Gas welding and argon arc welding of red copper. 機械性能好，抗裂性好。紫銅氣焊及氬弧焊用	ERCu
	S 211	Si3 Mn1 Cu Rem.	Good mechanical properties. Argon arc welding of copper alloys and MIG brazing of steel. 機械性能好，銅合金氬弧焊及鋼的MIG釬焊用	ERCuSi-Al
	S 212	Sn5 Cu Rem.	Wear resistance. Argon arc welding of copper alloys and surfacing of steel. 耐磨性好。銅合金氬弧焊及鋼的堆焊用	ERCuSn-A
	S 213	Sn8 Cu Rem.	Wear resistance. Argon arc welding of copper alloys and surfacing of steel. 耐磨性好。銅合金氬弧焊及鋼的堆焊用	ERCuSn-C
	S 214	Al7.5 Cu Rem.	Wear and corrosion resistance. Argon arc welding of copper alloys and surfacing of steel. 耐磨、耐蝕。銅合金氬弧焊及鋼的堆焊用	ERCuAl-A1
	S 215	Al9 Cu Rem.	Wear and corrosion resistance. Argon arc welding of copper alloys and surfacing of steel. 耐磨、耐蝕。銅合金氬弧焊及鋼的堆焊用	ERCuAl-A2
	S 221	Cu60 Sn1 Si0.3 Zn Rem.	Melting point is about 890℃. Gas welding and carbon arc welding of brass, also braze welding of copper, steel and cast iron. 熔點約890℃。黃銅氣焊及碳弧焊用，也可釬焊銅、鋼、鑄鐵
	S 221F	Cu60 Sn1 Si 0.3 Zn Rem.	S221 welding rod coated with flux. 外涂焊劑的S221焊絲
	S 222	Cu58Sn0.9Si0.1 Fe0.8 Zn Rem.	Melting point is about 880℃. Gas welding and carbon arc welding of brass, also braze welding of copper, steel and cast iron. 熔點約880℃。黃銅氣焊及碳弧焊用，也可釬焊銅、鋼、鑄鐵	RBCuZn-C
	S 222F	Cu58Sn0.9Si0.1 Fe0.8 Zn Rem.	S222 welding rod coated with flux. 外涂焊劑的S222焊絲	RBCuZn-C
	S 223	Cu59 Sn0.6 Zn Rem.	Melting point is about 900℃. Braze welding of copper, steel and cast iron. 熔點約900℃。銅、鋼、鑄鐵釬焊用	RBCuZn-A
	S 224	Cu62 Si0.5 Zn Rem.	Melting point is about 905℃. Gas welding and carbon arc welding of brass, also braze welding of copper, steel and cast iron. 熔點約905℃。黃銅氣焊及碳弧焊用，也可釬焊銅、鋼、鑄鐵
Copper alloys 銅 合 金	S 225	Cu48 Ni10 Zn Rem.	Melting point is about 935℃ and high strength. Braze welding of steel, nickel and carbide alloys. 熔點約935℃。高強度,釬焊鋼、鎳及硬質合金用	RBCuZn-D
	S 225F	Cu48 Ni10 Zn Rem.	S225 welding rod coated with flux. 外涂焊劑的S225焊絲	RBCuZn-D
	S 226	Cu60 Sn0.3 Si0.2 Zn Rem.	Melting point is about 900℃. Gas welding of brass, also braze welding of copper, steel and cast iron. 熔點約900℃。黃銅氣焊用，也可釬焊銅、鋼、鑄鐵
	S 227	Cu58Sn0.9Ni0.5 Si0.1 Fe0.8 Zn Rem.	Melting point is about 880℃. Gas welding and carbon arc welding of brass, also braze welding of copper, steel and cast iron. 熔點880℃。黃銅氣焊及碳弧焊用，也可釬焊銅、鋼、鑄鐵	RBCuZn-B
	S 229	Cu55 Ni6 Mn4 Zn余	Melting point is about 920℃, high strength. Braze welding of steel, nickel and hard carbide. 熔點約920℃。高強度,釬焊鋼、鎳及硬質合金用
Aluminum alloys 鋁 合 金	S 301	Al≥99.5	Good ductility and corrosion resistance. Gas welding and argon arc welding of pure aluminum. 塑性好、耐蝕。純鋁氣焊、氬弧焊用	ER1100
	S 311	Si5 Al Rem.	Corrosion resistance, wide range of usage. Gas welding and argon arc welding of aluminum alloys other than high magnesium alloys. 抗裂性好，通用性大。鋁合金氣焊、氬弧焊用。不宜用高鎂合金	ER4043
	S 321	Mn1.3 Al Rem.	Good corrosion resistance, weldability and ductility. Gas welding and argon arc welding of aluminum alloys. 良好的耐蝕性、可焊性及塑性。鋁合金氣焊、氬弧焊用
	S 331	Mg5 Mn0.4 Al Rem.	Corrosion resistance and high strength. Argon arc welding of aluminum alloys. 耐蝕，強度高。鋁合金氬弧焊用	ER5183