| 特 性 | 高鉻成份,耐磨耗耐龜裂性能優良,焊后硬度較高,機械加工困難. High chrome component, abrasion resistance, resistance to crack excellent performance after welding, machining difficulty high hardness. |
| 用 途 | 淬火硬化模具鋼刃口的修補,適用于SKD11合金工具鋼,淬火后的模具鋼修補. Quench hardened steel blade of repair, applicable to SKD11 alloy steel, alloy after quenching repair. |
| 規 格 | 2.6￠ 3.2￠ 4.0￠ |
CARBO 2M鑄鐵型面堆焊使用
| 特 性 | 可直接在鑄鐵上施焊,對于抗冷沖壓的金屬間磨耗非常有效.焊金第一層為奧氏體組織,從第二層開始為馬氏體組織抗磨耗性好. Can directly in the iron welding process, to make cold stamping metal abrasion very effective. Welding between the first layer of gold for austenitic group, second start martensite organization for good abrasion resistanceHRC46~52 |
| 用 途 | 球墨鑄鐵,火焰淬火鑄鐵,合金鑄鐵的直接堆焊. Ductile iron, flame hardening, alloy iron direct hardfacing. |
| 規 格 | 2.6￠ 3.2￠ 4.0￠ 5.0￠ |
CARBO 2H鑄鐵刃口堆焊使用
| 特 性 | 可直接在鑄鐵上施焊,對于抗冷沖壓的金屬間磨耗非常有效.焊金第一層為奧氏體組織,從第二層開始為馬氏體組織,抗磨耗沖壓性能優良. Can directly in the iron welding process, to make cold stamping metal abrasion very effective. Welding between the first layer of gold for austenitic group, second began to martensitic organization, abrasion resistance stamping excellent performance藍翔牌焊材 |
| 用 途 | 主要用于各種淬火后鑄鐵的刃口修補焊接. Mainly used for various hardened iron blade repair welding. |
| 規 格 | 2.6￠ 3.2￠ 4.0￠ 5.0￠藍翔牌焊材 |
GNK-61N鑄鐵焊條
| 特 性 | 有良好的抗拉強度和延伸率 硬度HB-160. Have good tensile strength and elongation hardness HB - 160. |
| 用 途 | 用于各種鑄鐵 合金鑄鐵 鋼與鑄鋼的焊接. For all kinds of iron alloy steel and cast iron welding. |
| 規 格 | 2.6￠ 3.2￠ 4.0￠ 5.0￠ |
GNK-67N焊條
| 特 性 | 用于不同鑄鐵焊接時焊層能要求的滿足其顏色匹配,抗拉強度和延展性優良. Used for welding of different iron welding layer can satisfy the requirements of color matching, tensile strength and ductility. |
| 用 途 | 焊補灰口鑄鐵,球墨鑄鐵. Weld-repair grey cast iron, ductile iron |
| 規 格 | 2.6￠ 3.2￠ 4.0￠ 5.0￠ |
GNK-8C打底焊條
| 特 性 | 高鉻成份,焊金具有高拉力,高韌性 HB-280. High chrome component, high strength, welding gold high toughness HB - 280.藍翔牌焊材 |
| 用 途 | 鑄鋼模硬面制做打底緩沖層,裂縫敏感度較高的特種鋼接合襯焊使用. Cast steel hardfaced making render buffer layer, crack sensitive use of special steel lining welding joints. |
| 規 格 | 2.6￠ 3.2￠ |